Application: For automobile parts
Technique: Cold-finished, hot-finished, ERW
Chemical composition:
Steel Grade | Chemical Composition % | ||||
C | Si | Mn | P | S | |
STAM 290GA | 0.12 max. | 0.35 max. | 0.60 max. | 0.035 max. | 0.035 max. |
STAM 290GB | |||||
STAM 340G | 0.20 max. | 0.35 max. | 0.60 max. | 0.035 max. | 0.035 max. |
STAM 390G | 0.25 max. | 0.35 max. | 0.30~0.90 | 0.035 max. | 0.035 max. |
STAM 440G | 0.25 max. | 0.35 max. | 0.30~0.90 | 0.035 max. | 0.035 max. |
STAM 440H | |||||
STAM 470G | 0.25 max. | 0.35 max. | 0.30~0.90 | 0.035 max. | 0.035 max. |
STAM 470H | |||||
STAM 500G | 0.30 max. | 0.35 max. | 0.30~1.00 | 0.035 max. | 0.035 max. |
STAM 500H | |||||
STAM 540H | 0.30 max. | 0.35 max. | 0.30~1.00 | 0.035 max. | 0.035 max. |
Mechanical Proporties:
Grade | Designation | Tensile strength | Yield Strength | Elongation (1)% No.1 test piece No.2 Test piece | Flaring test (2) |
Size of flared bell portion (D: outside diameter of tube) | |||||
{N/mm²} | {N/mm²} | Longitudinal direction | |||
Grade G | STAM 290GA | 30 min. | 18 min. | 40 min. | 1.25 D |
{294} min. | {177} min. | ||||
STAM 290GB | 30 min. | 18 min. | 35 min. | 1.20 D | |
{294} min. | {177} min. | ||||
STAM 340G | 35 min. | 20 min. | 35 min. | 1.20 D | |
{343} min. | {196} min. | ||||
STAM 390G | 40 min. | 24 min. | 30 min. | 1.20 D | |
{392} min. | {235} min. | ||||
STAM 440G | 45 min. | 31 min. | 25 min. | 1.15 D | |
{441} min. | {304} min. | ||||
STAM 470G | 48 min. | 33 min. | 22 min. | 1.15 D | |
{471} min. | {324} min. | ||||
STAM 500G | 51 min. | 36 min. | 18 min. | 1.15 D | |
{500} min. | {353} min. | ||||
Grade H | STAM 440H | 45 min. | 36 min. | 20 min. | 1.15 D |
{441} min. | {353} min. | ||||
STAM 470H | 48 min. | 42 min. | 18 min. | 1.10 D | |
{471} min. | {412} min. | ||||
STAM 500H | 51 min. | 44 min. | 16 min. | 1.10 D | |
{500} min. | {431} min. | ||||
STAM 540H | 55 min. | 49 min. | 13 min. | 1.05 D | |
{539} min. | {481} min. |